N08810 Nickel Alloy 90 Degree Elbow

Product Description

IntroductionSuper alloy VLX800H is a slightly modified version of Incoloy 800 with the 800H grade possessing higher creep and rupture strength. This modification is possible because of the closely controlled carbon content and modified heat treatment.The following sections will discuss in detail about super alloy VLX800H.Chemical CompositionThe chemical composition of super alloy VLX800H is outlined in the following table.

Element	Content (%)
Nickel, Ni	30 - 35
Chromium, Cr	19 - 23
Manganese, Mn	1.5 max
Silicon, Si	1 max
Copper, Cu	0.75 max
Aluminum, Al	0.15 - 0.6
Titanium, Ti	0.15 - 0.6
Carbon, C	0.05 - 0.1
Sulfur, S	0.015 max
Iron, Fe	Remainder

Physical Properties

The physical properties of super alloy VLX800H are tabulated below.

Properties	Metric	Imperial
Density	7.9 g/cm³	0.287 lb/in³
Melting point	1371°C	2500°F

Other DesignationsEquivalent materials to super alloy VLX800H are provided below:ASTM B163ASTM B407ASTM B408ASTM B409ASTM B514ASTM B564DIN 1.4876DIN 1.4958Fabrication and Heat TreatmentMachinabilitySuper alloy VLX800H can be machined using the common processes applied to iron based alloys. This alloy does work-harden during machining and displays higher strength and "gumminess" unlike steels. It is recommended that heavy duty machining equipment and tooling should be used to reduce chatter or work-hardening of the alloy.Any commercial coolants can be used during the machining operations; however water-based coolants are recommended for high-speed operations such as milling, turning, or grinding. Similarly, heavy lubricants are ideal for tapping, broaching, drilling, or boring.FormingSuper alloy VLX800H can be formed using any of the conventional methods as it is very ductile. Powerful equipment is required to perform forming operations as this alloy is strong. It is recommended that heavy-duty lubricants be used while performing cold forming. It is important to clean all traces of lubricant after forming.WeldingWelding of super alloy VLX800H can be performed using all the traditional welding methods. Matching alloy filler metal should be used. In case that is not available, it is advised that the nearest alloy closest to the chemical composition be used. The weld beads should be slightly convex, and preheating is not required. Surfaces to be welded have to be clean and free from oil, paint or crayon marking.ForgingForging should be performed in the temperature range of 1204-982°C (2200-1800°F).Hot WorkingHot working can be performed in the temperature range of 1204-871°C (2200-1600°F).Cold WorkingSuper alloy VLX800H can be cold formed using all the standard tools except for plain carbon tool steels as they produce galling.AnnealingSuper alloy VLX800H can be annealed at 1176°C (2150°F) and then air cooled.ApplicationsSuper alloy VLX800H is used in the following application areas:Piping for petrochemical plantsHeaters and heat exchangers that are used in prolonged high temperature environments.Stock

Form	Specification	Supply Form	Others
Sheet	Thickness:0.40-4.75mm,General Width:1000,1219,1500mm	Whole Coil or piece of it	Cold Annealed,Surface 2B,2E
Plate	Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,8000,8500mm(Under 10mm plate can be coiled)	Whole Coil or piece of it	Single hot rolling,Solid solution annealed state,Surface 1D
Belt	Thickness:0.10-3.0mm,Width:50-500mm	Whole Coil or Specified size	Cold Annealed,Surface 2B,2E
Bar & Rod	Rolled barΦ5-45mm,Length≤1500mm	Polished Bar(circle,Square)	Solution annealing,descaling
Bar & Rod	Forged barΦ26-245mm,Length≤4000mm	Polished Bar(circle,Square)	Solution annealing,descaling
Weld tube	Outer diameterΦ4.76-135mm,Wall Thickness0.25-4.00mm,Length:≤35000 mm	Base on your requirement	Use for PHE
Seamless Tube	Outer diameterΦ3-114mm,Wall Thickness0.2-4.5mm	Base on your requirement	Use for PHE
Wire	Outer diameterΦ0.1-13mm	Base on your requirement	Ni & Ni alloy, Ti & Ti alloy
Forged piece	roundness and square alloy	Base on your requirement	Steel, Alloy
Flangs	All kinds of Flangs	Base on your requirement	Steel, Alloy
Welding Material	Coil wire Φ0.90mm/1.2mm/1.6mm	Base on your requirement	Certificate of Origin:America, Sweden, Britain, Germany, Austria, Italy, France.
	Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm
	Welding rodΦ2.4mm/3.2mm/4.0mm
Tube	Elbow, three links, four links, different diameter size	Base on your requirement	Ni & Ni alloy, Ti & Ti alloy
Explosive bonded laminate	Raw Sheet Thickness≥2mm	Base on your requirement	Ni & Ni alloy, Ti & Ti alloy

Contact us if you need more details on N08810. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Incoloy 800h、Elbow. If these products fail to match your need, please contact us and we would like to provide relevant information.